Reduction of edge effects from aspect ratio trapping

ABSTRACT

A device includes a crystalline material within an area confined by an insulator. In one embodiment, the area confined by the insulator is an opening in the insulator having an aspect ratio sufficient to trap defects using an ART technique. Method and apparatus embodiments of the invention can reduce edge effects in semiconductor devices. Embodiments of the invention can provide a planar surface over a buffer layer between a plurality of uncoalesced ART structures.

RELATED APPLICATIONS

This application is a continuation of U.S. patent application Ser. No. 13/591,603, filed Aug. 22, 2012, entitled “REDUCTION OF EDGE DEFECTS FROM ASPECT RATIO TRAPPING,” which is a divisional of U.S. patent application Ser. No. 12/495,161, filed Jun. 30, 2009, entitled “REDUCTION OF EDGE DEFECTS FROM ASPECT RATIO TRAPPING,” which claims the benefit of and priority to U.S. Provisional Application No. 61/077,462 filed Jul. 1, 2008, entitled “REDUCTION OF EDGE EFFECTS FROM ASPECT RATIO TRAPPING” and U.S. Provisional Application No. 61/077,465 filed Jul. 1, 2008, entitled “A SEMICONDUCTOR DEVICE AND METHOD OF MAKING THE SAME;” the disclosures of these applications are hereby incorporated by reference in their entireties.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to semiconductor structures or device fabrication using lattice mismatched materials.

2. Description of the Related Art

This section provides background information and introduces information related to various aspects of the disclosure that are described and/or claimed below. These background statements are not admissions of prior art.

Integration of lattice mismatched semiconductor materials is one path to high performance semiconductor devices such as complementary metal-oxide-semiconductor (CMOS) field-effect transistors (FET) due to their high carder mobility. For example, the heterointegration of lattice mismatched semiconductor materials with silicon will be useful for a wide variety of device applications. However, disadvantages associated with structural characteristics of related art lattice mismatched devices can decrease device performance, require additional processes or design constraints to counter-effect such structural characteristics or reduce manufacturing yields. Thus, there exists a need for semiconductor structures that provide high performance lattice mismatched materials, for example in an active region of a device.

SUMMARY OF THE INVENTION

Embodiments according to the present invention provide methods, structures and apparatus to reduce edge effects of lattice mismatched materials.

Embodiments according to the present invention provide methods, structures and apparatus to reduce edge effects or edge related disadvantages of aspect ratio trapping (ART) techniques suitable or device fabrication and/or devices made thereby.

In one aspect, one embodiment of the invention can provide an above-pattern planar buffer layer to reduce or eliminate effects of physical edges of the heteroepitaxial regions (e.g., Ge regions).

In another aspect, one embodiment of the invention can provide ART structures with reduced or low levels of edge leakage characteristics and/or surface recombination characteristics.

In another aspect, one embodiment of the invention can provide ART structures with reduced or low levels of three dimensional feature inaccuracies and/or layer dimension differences.

In another aspect, one embodiment of the invention can provide co-planar un-coalesced ART structures, above-pattern un-coalesced ART structures or above-pattern coalesced ART structures with an above-pattern planar buffer layer.

In yet another aspect, one embodiment of the invention can provide an ART structure continuous layer with a single type planar layer.

In yet another aspect, one embodiment of the invention can provide an ART structure continuous layer with a single type planar layer that can function as a conventional bulk substrate.

These aspects may be especially applicable to devices incorporating ART techniques, including but not limited to a mixed signal application device, a field effect transistor, a quantum-tunneling device, a light emitting diode, a laser diode, a resonant tunneling diode and a photovoltaic device. The ART devices may have crystalline material epitaxially grown in openings or confined areas with an aspect ratio (depth/width) >0.5, or otherwise suitable for trapping most defects.

In accordance with one aspect of the present invention, there is provided a semiconductor structure that can include a crystalline substrate, an insulator pattern having an opening to the substrate, a crystalline material within the opening in the insulator, the crystalline material being lattice-mismatched with the substrate and an single type planar layer over the insulator pattern.

Additional aspects and utilities of the invention will be set forth in part in the description which follows and, in part, will be obvious from the description, or may be learned by practice of the invention.

BRIEF DESCRIPTION OF THE DRAWINGS

These and/or other aspects and utilities of the present general inventive concept will become apparent and more readily appreciated from the following description of the embodiments, taken in conjunction with the accompanying drawings, of which:

FIG. 1, comprising FIGS. 1( a)-1(c), respectively illustrate (a) cross-sectional TEM image of defect trapping in ART structure (e.g., 200 nm trenches of Ge) where a lattice mismatch material region above the dashed line has reduced defects, (b) schematic of an exemplary device structure showing ART reduced crystalline defects, and (c) an exemplary alternate configuration (e.g., confined area for crystalline material) of ART structure.

FIG. 2 comprising FIGS. 2 a-2 c respective y illustrate exemplary ART structures.

FIG. 3 comprising FIGS. 3 a-3 c respectively illustrate selected exemplary disadvantages associated with exemplary ART structures.

FIG. 4 illustrates top plan view of an exemplary ART structure.

FIG. 5 illustrates an exemplary embodiment of an above-pattern planar layer in an ART structure.

FIG. 6 illustrates an exemplary embodiment of as planar buffer layer in an ART structure.

FIG. 7 comprising FIGS. 7 a-e, respectively illustrate exemplary formation of amorphous or poly silicon materials corresponding to crystalline structures configured to form an embodiment of a planar layer.

FIG. 8 is a diagram illustrating an embodiment of a method for forming a semiconductor device according to the invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

Reference will now be made in detail to the embodiments of the present general inventive concept, examples of which are illustrated in the accompanying drawings, wherein like reference numerals refer to like elements throughout. The embodiments are described below in order to explain the present general inventive concept by referring to the figures.

The formation of lattice-mismatched materials has many practical applications. For Example, heteroepitaxially growth of group IV materials or compounds, and III-V, III-N and II-VI compounds on a crystalline substrate, such as silicon has many applications such as photovoltaics, resonant tunneling diodes (RTD's), transistors (e.g., FET (which can be planar or 3D (e.g., finFET), HEMT, etc.), light-emitting diodes and laser diodes. As one example, heterospitaxy of germanium on silicon is considered a promising oath for high performance p-channel metal-oxide-semiconductor (MOS) field-effect transistors (FET) and for integrating optoelectronic devices with silicon complementary MOS (CMOS) technology. Heteroepitaxy growth of other materials (e.g., of group III-V, III-N and II-VI compounds and other group IV materials or compounds) also is beneficial for these and ether applications.

However, the dislocation density of the epitaxially grown material can be unacceptably high for many applications. For example, the dislocation density of germanium directly grown on silicon can be as high as 10⁸-10⁹ cm⁻² due to the 4.2% lattice mismatch between the two materials—unacceptable for most device applications. Various approaches to reducing the defect density have been pursued, including compositional grading and post-epi high-temperature annealing. However, these approaches may not be optimal for integration with silicon-based CMOS technology due to requirements for thick epi-layers and/or high thermal budgets, or due to incompatibility with selective growth at a density suitable for CMOS integration.

Aspect Ratio Trapping (ART) is a defect reduction technique that mitigates these problems. As used herein, “ART” or “aspect ratio trapping” refers generally to the technique(s) of causing defects to terminate at non-crystalline, e.g., dielectric sidewalls, where the sidewalls are sufficiently high relative to the size of the growth area so as to trap most, if not all, of the defects. ART utilizes high aspect ratio openings, such as trenches or holes, to trap dislocations, preventing them from reaching the epitaxial film surface, and greatly reduces the surface dislocation, density within the ART opening.

FIG. 1 a snows a cross section of an exemplary lattice mismatched material 140 of high quality above a defect region 155 using ART. As illustrated he a crystalline material 140 is epitaxially grown on substrate 100 (e.g., on the (001) surface of a silicon substrate). By confining the crystalline growth within an opening (e.g., trench, recess or the like) in a non-crystalline material with a sufficiently high aspect ratio (e.g., 1 or greater, 0.5 or greater), defects 150 formed while epitaxially growing the crystalline material 140 travel to and end at the sidewalls (e.g., insulator sidewalls)130. It is noted that depending upon different amounts of mismatch between lattices of crystalline structure and substrate, as well as the orientation of the crystal surface to the crystalline structure, the opening may have different aspect ratios and/or different dimensions for obtaining structure 140 with satisfied quality. The crystalline material 140 continues to grow without the continued growth of the defects 150 (e.g., above region 155), thereby producing crystal with reduced defects. This technique has been shown to be effective for growing low defectivity materials such as Ge, InP and GaAs selectively on Si in trenches 200-450 nm wide and of arbitrary length—an area large enough for devices such as an FET, for example. Such trenches can be wider or narrower.

An embodiment of the invention is directed to a device including a lattice mismatched material in an opening in an insulator. FIG. 1 b shows one example, illustrating a perspective view of a portion of an exemplary device. As shown in FIG. 1 b, a crystalline material 140 is at a substrate 100 in an opening 120 defined in an insulator 110 fore non-Si channel MOSFET. Portions of the crystalline material 140 can correspond to source, drain and channel regions of the device.

The substrate 100 may be, for example, a bulk silicon wafer, a bulk germanium wafer, a semiconductor-on-insulator (SOI) substrate, or a strained semiconductor-on-insulator (SSOI) substrate. The substrate 100 may include or consist essentially of a first semiconductor material, such as a group IV element, e.g., Ge or Si. In on embodiment, substrate 100 includes or consists essentially of (100) silicon. However, alternative crystal orientations may be used. A non-crystalline material, such as an insulator or a dielectric layer 110, is formed over the semiconductor substrate 100. The dielectric; layer 110 may include a dielectric material, such as silicon nitride or silicon dioxide. The dielectric layer 110 may be formed by a method known to one of skill in the art, e.g., thermal oxidation or plasma-enhanced chemical vapor deposition. As discussed below, the dielectric layer may have a thickness corresponding to a desired height (e.g., 25 nm to 2000 nm) of crystalline material to be deposited in an opening formed through the dielectric layer. A mask such as a photoresist mask, can be formed over the substrate 100 and the dielectric layer 110. The mask can be patterned to expose at least a portion of the dielectric layer 110. The exposed portion of the dielectric layer 110 is removed, e.g., by reactive on etching (RIE), to define an opening 120, which can extend to a surface of the substrate 100 and may be defined by at least one insulator sidewall 130, e.g., a non-crystalline sidewalk.

In one example, the width of the opening 120 may be 400 nm or less, 350 nm or less or 200 nm or less, 100 nm or less or 50 nm or less; these sizes have been shown to be effective for ART (of course these sizes do not need to be used with to ART). Alternatively, the width of the opening may be 5 um or less. In another alternative, the width of the opening may be 1 um or less. The opening may be formed as a trench (with the length of the trench running front to back as shown in FIG. 1 b) in which case the width would be considered to be perpendicular to its length and height. The length of the trench may be arbitrary. Alternatively, the length of the trench may be substantially larger than the width of the trench, for example greater than 10 times larger, or greater than 100 times larger. In one example, the length of the trench is 2 um.

It is preferred, but not necessary, that the opening 120 is used to trap defects when epitaxially growing the crystalline material 140 using ART (aspect ratio trapping) techniques. In such a case, the aspect ratio (AR—height/width) may be greater than 1, although it possible for the aspect ratio to be lower in ART devices, for example, the AR can be 0.5. (Aspect ratio “AR” is defined for trenches as the ratio of the trench height/trench width.) Further details of example ART devices and ART techniques in which this invention may be incorporated may be found in U.S. patent application Ser. No. 11/436,198 filed May 17, 2006, Ser. No. 11/4193,365 filed Jul. 26, 2006 and Ser. No. 11/852,078 filed Sep. 7, 2007, all of which are hereby incorporated by reference.

The substrate 100 in the above examples may include a group IV element or compound, such as germanium and/or silicon, e.g., (100) silicon. The crystalline material 140 may include at least one of a group IV element or compound, a III-V or III-N compound, or a II-VI compound. Examples of group IV elements include Ge, Si and examples of group IV compounds include SiGe. Examples of III-V compounds include aluminum phosphide (AlP), gallium phosphide (GaP), indium phosphide in (InP), aluminum arsenide (AlAs), gallium arsenide (GaAs), indium arsenide (InAs), aluminum antimonide (AlSb), gallium antimonide (GaSb), indium antimonide (InSb), and their ternary and quaternary compounds. Examples of III-N compounds include aluminum nitride (AlN), gallium nitride (GaN), indium nitride (InN), and their ternary and quaternary compounds. Examples of II-VI compounds includes zinc selenide (ZnSe), zinc telluride (ZnTe), cadmium selenide (CdSe), cadmium telluride (CdTe), zinc sulfide (ZnS), and their ternary and quaternary compounds.

The crystalline semiconductor material 140 may be formed by selective epitaxial growth in any suitable epitaxial deposition system, including, but not limited to, metal-organic chemical vapor deposition (MOCVD), atmospheric-pressure CVD (APCVD), low- (or reduced-) pressure CVD (LPCVD), ultra-high-vacuum CVD (UHVCVD), molecular beam epitaxy (MBE), or atomic layer deposition (ALD). In the CVD process, selective epitaxial growth typically includes introducing a source gas into the chamber. The source gas may include at least one precursor gas and a carrier gas, such as, for example hydrogen. The reactor chamber may be heated by, for example, RF-heating. The growth temperature in the chamber may range from about 300.degree. C. to about 1100.degree. C., depending on the composition of the crystalline material and the desired growth rate. The growth system may also utilize low-energy plasma to enhance the layer growth kinetics.

Tie epitaxial growth system may be a single-wafer or multiple-wafer batch reactor. Suitable CVD systems commonly used for volume epitaxy in manufacturing applications include, for example, an Aixtron 2600 multi-wafer system available from Aixtron, based in Aachen, Germany; an EPI CENTURA single-wafer multi-chamber systems available from Applied Materials of Santa Clara, Calif.; or EPSILON single-wafer epitaxial reactors available from ASM International based in Bilthoven, The Netherlands.

Dislocation defects 150 in the crystalline semiconductor material 140 reach and terminate at the sidewalls of the opening 120 in the dielectric layer 110 at or below a prescribed vertical distance from the surface of the substrate, such that dislocations in the crystalline material 140 decrease in density with increasing distance from the bottom portion of the opening 120. Accordingly, the bottom portion of the second crystalline semiconductor material 140 comprises lattice defects, and the upper portion of the crystalline material is substantially exhausted of crystalline defects. Various crystalline defects such as threading dislocations, stacking faults, twin boundaries, or anti-phase boundaries may thus be substantially eliminated from the upper portion of the crystalline material.

The layer of insulator need not be formed as a substantially planar layer. For example, the insulator may be formed of a thin layer that conforms to a surface of the substrate on which it is provided or deposited. FIG. 1 c illustrates an example including a substrate that has openings/recesses/trenches 120 etched into the substrate 100. An insulating layer 110′ has been formed across the substrate 100 conforming to the surface topography of the etched substrate 100. The insulating layer 110′ is configured at the bottom of the openings/trenches to expose portions 160 of the substrate 100 for subsequent lattice mismatched crystalline material. In this case, sidewalls of the insulator 130′ can be formed from the outer surface of the insulator 110 after its deposition and are not formed by a separate photolithography and etch process. Exemplary configurations o the openings 120 and portions 160 are illustrated however, embodiments of the invention are not intended to be an limited, for example, as other linear, tiered or nonlinear cross-sections may be used for the openings 120 and the portions 160.

The following description in connection with FIGS. 2-8 describes examples of how the lattice mismatched semiconductor material or crystalline material within a confined space (e.g., crystalline material 140 within insulator 130) may be modified to improve an electrical or structure/device performance characteristics (e.g., reduce edge-related disadvantages). Although this description is in connection with specific materials and process parameters, it will be apparent that the description is exemplary only, and should not be considered to limit the invention to such materials and process parameters.

Three exemplary ART configurations are illustrated n FIGS. 2 a-2 c. Such ART structures include reduced defect crystalline materials 210 provided partially within insulator patterns 220. FIG. 2 a illustrates a co-planar un-coalesced ART structure. FIG. 2 b illustrates an above-pattern tin-coalesced ART structure, and FIG. 2 c illustrates an above-pattern coalesced ART structure that includes coalescence boundaries 225.

When using coalesced and un-coalesced ART structures, the presence of the ART edges can lead to various potential performance degradation effects. Further, when using coalesced and un-coalesced ART structures, the presence of the ART edges can lead to various fabrication process disadvantages.

For example, the un-coalesced ART materials can be considered separate features or individual islands (including peninsulas, strips, segments, or other geometric forms) when using un-coalesced ART structures (e.g., co-planar or above-pattern) for device/integrated circuit fabrications. As individual features, there is a difficulty in providing additional device layers on/over/covering the ART structure. Such additional device layers involve difficulties such as three-dimensional (3D) dimension issues for subsequent device features over the un-coalesced ART structures, edge/interface issues or resistance issues. For example, when epitaxially growing additional device layers there are 3D dimension issues because such intended 3D feature configurations can not be accurately provided over the ART structure. FIG. 3 a is a diagram that illustrates exemplary disadvantages relating to 3D feature issues can include faceting difficulties that can occur over separate flat ART top surfaces or on/over the island edges. Further, inaccurate top outer dimensions (e.g., corners), film thickness differences between areas proximate/over an edge and center areas (e.g., epitaxial film thicknesses) can also occur. For example, in a vertical layout of a P-I-N photodiode, corner and continuous vertical side 3D dimensions of a multi-plane top electrode over a rectangular intrinsic layer are very difficult to achieve.

In addition, the separate ART structures may increase the fabrication process complexity of subsequent device fabrication and integrated circuit fabrication. Although selected disadvantages with various ART structures are discussed herein, these are intended to be exemplary and not limiting.

Potential edge related issues include leakage issues, either with or without additional device layer(s) (e.g., epitaxial layers). Such edge related issues may require additional edge isolation remedial processes, which can increase required tolerances or add fabrication procedures. Additional potential edge-related or trench-pattern-related disadvantages include surface recombination (e.g., at an and surface or epitaxial-dielectric interface) of additional device layers or increased series resistance for selected device applications. FIG. 3 c is a diagram that illustrates top and perspective views of an exemplary ART structure capable of use with solar cells. As shown in FIG. 3 c, in an application for solar cells (e.g., p-n diodes) with ART structure, dielectric patterns and the trenched-pattern structure can (i) increase the parasitic sales resistance of the p-n diode (325) and/or (ii) can lead to efficiency loss due to surface recombination at the edge/semiconductor-dielectric interlace.

As the intent is to locate a circuit or device at the crystalline material of the ART structure, edges or interfaces of concern can occur between semiconductor material and insulator materials. As shown in FIG. 3 b, exemplary edge disadvantages can result from edges that can occur between crystalline material and air or between crystalline material and dielectric patterns. Such edges can result in device design dependent disruptive leakage issues including leakage currents. For example, in a vertical layout of a P-I-N photodiode, a distance between a N+ bottom and a P+ top electrode around an intrinsic crystalline material layer may be very small, which may lead to breakdown leakage current. In addition, surface recombination can occur at an edge or throughout an entire semiconductor/dielectric interface and can result in efficiency loss for some optoelectronic devices or energy devices. For example, when dimensions of the P-I-N photodiode intrinsic layer cross a layout oxide pattern, efficiency of he photodetector can be reduced by resultant corresponding surface recombination at that location.

FIG. 4 illustrates a top plan view of an above pattern coalesced ART structure to illustrate coalesced regions C1 and C2. Such coalesced regions C1 and C2 include more than one defect trapping region or opening corresponding to one continuous reduced defect crystalline material region. As shown in FIG. 4, edge-related disadvantages may occur at a coalesced region/pattern region interface for such an above pattern coalesced ART structure.

Embodiments of the application provide methods, structures or apparatus to reduce or eliminate edge related disadvantages for un-coalesced and coalesced ART structures. In one embodiment, an above-pattern planar buffer layer can be generated to reduce or eliminate selected physical edges for un-coalesced and coalesced ART structures or corresponding device. In embodiments of the application, an planar buffer layer can cover a co-planar un-coalesced ART structure or fill in areas between an above-pattern un-coalesced ART structure. Thus, an embodiment of an above-pattern planar buffer layer can be continuous for both co-planar un-coalesced ART structure and an above-pattern un-coalesced ART structure. According to embodiments, material quality, and even the type of the material, in those additional areas may not be critical to address such edge related issues. Further, proximate regions to edges or edge areas may not all be intended to be used for subsequent device/IC functional elements (e.g., active device region). Depending upon the specific semiconductor device, functional elements can be of different natures. For example, functional elements can be a channel of a transistor (e.g., a metal-oxide-silicon field-effect-transistor), or a PN junction or a PIN junction of a diode, the source or drain of the transistor, or the P contact or the N contact of the diode. In an alternative example, functional elements can be an isolator, such as a shallow-trench-isolator or a mesa isolator, which may be formed adjacent to low defect crystalline material. However, one exemplary reason for a continuous above-pattern planar buffer layer is to reduce or eliminate physical edges between crystalline materials and insulators.

As shown in FIG. 5, additional regions 510, 520, 530, 540, 550 can form an exemplary planar buffer layer. In one embodiment, a top surface of the above pattern planar buffer layer is co-planar with a top surface of the above pattern un-coalesced ART structure. In one embodiment, planar buffer layers can he of one material. Thus, materials in regions 510, 530, 540, 550 may be the same as materials in device areas or region 520. Thus, a high quality epitaxial material may be used for regions 510, 520, 530, 540, 550. In another embodiment, materials in region 520 (e.g., a device region) may be different from regions 510, 530, 540, 550. In one embodiment, the material for regions 510, 520, 530, 540, 550 has a higher defect level than the material for region 520 (or regions 580, 565). Here, for example, regions 510, 530, 540, 550 may be one material such as Si or SiGe when the material in the device area 520 is a different material Ge. Alternatively, regions 510, 530, 540, 550 may be Ge when the material in the device area 520 is III-V.

The materials in these additional regions 510, 520, 530, 540, 550 may he formed by various materials. For example, materials in the additional regions 510, 530, 540, 560 may be provided by amorphous material or polycrystalline material. Semiconductor materials for devices may have a wide range of different as of defects, such as point defects (e.g. vacancies, impurities, and topological defects), line defects (e.g. dislocations and disinclinations), planar defects (e.g. grain boundaries defects and stacking fault defects), hulk defects (e.g. voids and cluster impurities), and many other types of defects. Dopants are typically added to a semiconductor material to increase its charge carriers (electrons or holes); as is understood in the art, and for the purpose of this application, defects are not considered to include dopants. Different semiconductor devices or different functional members of a specific semiconductor device can be vulnerable to different types of defects. Although amorphous semiconductor materials are good materials for certain applications, for this application, we consider amorphous materials to be very defective. Amorphous semiconductor material is full of dangling bonds. Dangling bonds and other defects in the amorphous semiconductor material may degrade the device performance significantly compared to the use of single crystal semiconductor material. Polycrystalline semiconductor material is also considered a more defective material compared to the single crystal semiconductor materials but less defective than amorphous semiconductor material. Grain-boundaries in the polycrystalline semiconductor material are defects, and the electrical and optical properties of polycrystalline silicon films are dominated by those grain-boundaries defects. In one embodiment, materials in the additional regions 510, 530, 540, 550 may have greater defects levels (e.g., dislocation defects) than the materials in the additional region 520 (e.g., or regions 580 or 585).

According to the application, embodiments of additional above-pattern planar semiconductor buffer layers may need selected dimensions such as thickness to be greater than a prescribed thickness, (e.g., thin SOI), such that the dielectric pattern underneath and its interface with an exemplary buffer layer will not negatively impact a corresponding device and/or fabrication processes may proceed procedurally similar to the conventional planar process.

For example, a dimension such as minimum thickness requirement can be varied corresponding to the device fabrication technology being used. For example, in fabricating 65 nm technology nodes of CMOS devices, a minimum thickness of 12.5 nm may be required so that a full functional source or drain contact region can be built. For fabricating 45 nm technology nodes of CMOS devices, a minimum thickness of 9 nm may be required.

Such semiconductor buffer layer formation can be performed by known techniques. An amorphous or poly-crystalline or single-crystalline semiconductor buffer layer may be deposited by various techniques known to those skilled in the art, for example, an amorphous or polycrystalline film deposited by chemical vapor deposition (CVD) processes, or a lateral epitaxy layer grown from the adjacent ART structure by CVD process.

FIG. 6 illustrates another exemplary embodiment according to the application. According to one embodiment, exemplary ART structures resemble the conventional bulk substrate after adding such an additional above-pattern planar semiconductor buffer layer. Thus, an exemplary structure 670 has a planarized continuous layer of one type. In this case, subsequent device/IC fabrication may proceed in a manner similar to the conventional planar process. In one embodiment, an additional device layer 650 may be added.

A method embodiment for manufacturing a semiconductor device having a first planar layer over a crystalline material confined in at least one recess defined by an insulator will now be described with reference to FIG. 8. The embodiment will be described using and can be applied to device embodiments herein; however, the method embodiment of FIG. 8 is not intended to be limited thereby.

As shown in FIG. 8, after a process starts, a crystalline material is grown within recesses over a lattice mismatched substrate until a surface of the crystalline material is above a surface of an insulator (operation block 810). The crystalline material greater than a prescribed height over the substrate or over a top surface of the insulator preferably has reduced defects. For example, the crystalline material may be provided using ART techniques. A shown in exemplary FIG. 7 a, the crystalline material 702, 706 may have a distinctive mushroom caps) in crystalline material above the insulator.

Additional semiconductor materials can be provided to fill exposed areas over the insulator or to fill the gaps between the crystalline material (e.g., projecting crystalline material or ART islands) (operation block 820). Preferably, the additional material can reduce or eliminate at least disadvantages related to edges between crystalline material and insulators. In one embodiment, the additional semiconductor materials can include a polycrystalline material, amorphous material, or a single-crystal, which may be example provided by lateral epitaxial growth under controlled environment conditions from the ART islands. In an embodiment as shown in FIG. 7 b, the additional materials are up to approximately less than half a height of the mushroom caps, approximately a height of a resultant planar layer or a prescribed height greater than a subsequent planar layer. Alternatively, in an embodiment as shown in FIG. 7 c, the additional materials are provided to a height over or a prescribed amount above a height of the mushroom caps.

Then, as shown in FIG. 8, a buffer layer can be farmed by planarizing the additional material (operation block 830) (e.g., CMP structures of FIGS. 7 b or 7 c). In one embodiment, the additional materials can form a buffer layer with the crystalline material 706. It is preferred that the top surface of the buffer layer (which can include multiple isolated and/or interconnected segments, strips, islands, peninsulas, and/or other geometric forms) and the top surface of the ART structure form a substantially continuous and substantially flat surface. In one example, the buffer layer can include a semiconductor material or an electrically conductive material. The buffer layer can be crystalline, amorphous, poly-crystalline, or other types of structures. Then, a device can be completed (operation block 840). Such device fabrication can be implemented using previously described techniques. Further, one method for device fabrication according to FIG. 8 can be integrated with a CMOS process, in an embodiment as shown in FIG. 7 e, additional device epitaxial layer(s) may be grown or provided before device fabrication of operation block 840.

In one embodiment the first crystalline material is a lattice mismatched semiconductor material. In another embodiment, the first crystalline material has a coalesced top surface connecting first crystalline material from a plurality of adjacent recesses. In one embodiment the recess is a hole, trench, or a plurality trenches each having a prescribed cross-section. In one embodiment, the insulator has an opening to a substrate of a second crystalline material lattice mismatched to the first crystalline material. In one embodiment, the first crystalline material confined in the recess defined by the insulator was formed using ART techniques. In one embodiment, the second crystalline material may include a group IV element or compound, such as germanium and/on silicon, and the first crystalline material may include at least one of a group IV element or compound, a III-V or III-N compound, or a II-VI compound.

As described above, embodiments of methods for manufacturing devices, and devices made thereby can provide a single type planar layer. Accordingly, in one embodiment, the planar layer can operate as a conventional bulk substrate.

As described above, embodiments of structures and devices, and methods for the same can provide various advantages. For example, by adding an above-pattern planar buffer layer according to disclosed embodiments, additional device layer(s) may be provided (e.g., grown) without the issues of 3D faceting on the ART structures edges. Further, using an embodiment of an above-pattern planar semiconductor buffer, non-uniformity of film thickness (e.g., epitaxial film) over edge of ART crystalline material or ART structures can be reduced or prevented. In addition, device/IC fabrication can be performed without potential edge leakage and isolation issues using disclosed embodiments of methods, structures and devices. Further, fabrication process on ART substrates may become simpler, and/or can use procedures of a planar IC process approach.

Another advantage of embodiments of this novel structure is that ART film produced by ART techniques does not function as isolated structures or islands. Embodiments of an ART film can function as or become a continuous semiconductor film, which can resemble features of bulk substrate or continuous coalesced-ART structure in this aspect. For example, functional elements of semiconductor devices can be formed by treating the ART structures, the buffer aver, the patterned dielectric layer, and the substrate as a bulk substrate.

As noted above, this invention has a wide variety of applications. While not limited to ART technology, this invention has many applications within ART technology. For example, use of this invention may be used to create strained Ge over a SiGe alloy grown in an opening within an insulator. One or both of the Ge and SiGe layers may be grown in accordance with the invention and/or may have a surface of reduced roughness. A wide variety of devices may incorporate the invention. While not limiting to these devices, the invention may be particularly applicable to mixed signal applications, field effect transistors, quantum tunneling devices, light emitting diodes, laser diodes, resonant tunneling diodes and photovoltaic devices, especially those using ART technology. Application Ser. No. 11/857,047 filed Sep.; 18, 2007 entitled “Aspect Ratio Trapping for Mixed Signal Applications”; application Ser. No. 11/861,931 filed Sep. 28, 2007 entitled “Tri-Gate Field-Effect Transistors formed by Aspect Ratio Trapping”; application Ser. No. 11/862,850 filed Sep. 27, 2007 entitled “Quantum Tunneling Devices and Circuits with Lattice-mismatched Semiconductor Structures”; application Ser. No. 11/875,381 filed Oct. 19, 2007 entitled “Light-Emitter-Based Devices with Lattice-mismatched Semiconductor Structures”; and application Ser. No. 12/100,131 filed Apr. 9, 2007 entitled “Photovoltaics on Silicon” are all hereby incorporated by reference as providing examples to which aspects of this invention may be particularly suited.

A silicon CMOS device may be processed prior to embodiments of the invention, therefore, embodiment of devices such as LEDs or photovoltaic devices according to the invention integrated with CMOS process may be fabricated. Further, structures and/or methods according to disclosed embodiment can be used for high mobility, non-Si channel MOSFETs for next generation CMOS and for a wide variety of other applications.

Any reference in this specification to “one embodiment,” “an embodiment,” “example embodiment,” etc., means that a particular feature, structure, or characteristic described in connection with the embodiment is included in at least one embodiment of the invention. The appearances of such phrases in various places in the specification are not necessarily all referring to the same embodiment. Further, when a particular feature, structure, or characteristic is described in connection with any embodiment. It is submitted that it is within the purview of one skilled in the art to affect such feature, structure, or characteristic in connection with other ones of the embodiments. Furthermore, for ease of understanding, certain method procedures may have been delineated as separate procedures; however, these separately delineated procedures should not be construed as necessarily order dependent in their performance. That is, some procedures may be able to be performed in an alternative ordering, simultaneously, etc. In addition, exemplary diagrams illustrate various methods in accordance with embodiments of the present disclosure. Such exemplary method embodiments are described herein using and can be applied to corresponding apparatus embodiments, however, the method embodiments are not intended to he limited thereby.

Although few embodiments of the present invention have been illustrated and described, it would be appreciated by those skilled in the art that changes may be made in these embodiments without departing from the principles and spirit of the invention. The foregoing embodiments are therefore to be considered in all respects illustrative rather than limiting on the invention described herein. Scope of the invention is thus indicated by the appended claims rather than by the foregoing description, and all changes which come within the meaning and range of equivalency of the claims are intended to be embraced therein. As used in this disclosure, the term “preferably” is non-exclusive and means “preferably, but not limited to.” Terms in the claims should be given their broadest interpretation consistent with the general inventive concept as set forth in this description. For example, the terms “coupled” and “connect” and derivations thereof) are used to connote both direct and indirect connections/couplings. As another example, “having” and “including”, derivatives thereof and similar transitional terms or phrases are used synonymously with “comprising” all are considered “open ended” terms)—only the phrases “consisting of” and “consisting essentially of” should be considered as “close ended”. Claims are not intended to be interpreted under 112 sixth paragraph unless the phrase “means for” and an associated function appear in a claim and the claim fails to recite sufficient structure to perform such function. 

What is claimed is:
 1. A structure comprising: a substrate comprising a first crystalline material; a dielectric layer defining at least a first opening and a second opening to the substrate; a first region of a second crystalline material in the first opening and extending above the first opening, the second crystalline material being lattice mismatched to the first crystalline material, defects arising from the lattice mismatch within the first region terminating at a sidewall of the first opening, the first region having a first lateral edge above the dielectric layer; a second region of the second crystalline material in the second opening and extending above the second opening, defects arising from the lattice mismatch within the second region terminating at a sidewall of the second opening, the second region having a second lateral edge above the dielectric layer; a third material over the dielectric layer and disposed between the first lateral edge and the second lateral edge, the second crystalline material in respective portions of the first region and the second region above the dielectric layer being less defective than the third material; and a device formed in and/or above at least one of the first region and the second region.
 2. The structure of claim 1, wherein the third material is a different material from the second crystalline material.
 3. The structure of claim 1, wherein the third material is amorphous.
 4. The structure of claim 1, wherein the third material is polycrystalline.
 5. The structure of claim 1, wherein no device is formed in the third material.
 6. The structure of claim 1 further comprising a planar device layer over the second crystalline material and the third material, the device being formed at least partially in the planar device layer.
 7. A structure comprising: a substrate comprising a first crystalline material; a dielectric layer over the substrate and having a top surface, the dielectric layer defining at least a first opening from the top surface to the substrate; a first region of a second crystalline material in the first opening, the second crystalline material being lattice mismatched to the first crystalline material, defects arising from the lattice mismatch within the first region terminating at a sidewall of the first opening; a second region of a third crystalline material over the first region, the second region having a first lateral edge extending higher than the top surface of the dielectric layer; a third region of a fourth material over the dielectric layer and disposed adjacent the first lateral edge, the third crystalline material in the second region being less defective than the fourth material; and a device formed in and/or above the second region.
 8. The structure of claim 7, wherein the second crystalline material and the third crystalline material are a same crystalline material.
 9. The structure of claim 7, wherein the second crystalline material and the third crystalline material are different crystalline materials.
 10. The structure of claim 7, wherein the second region of the third crystalline material comprises a strain, the first region of the second crystalline material inducing the strain.
 11. The structure of claim 7, wherein the fourth material is amorphous.
 12. The structure of claim 7, wherein the fourth material is polycrystalline.
 13. The structure of claim 7 further comprising a planar device layer over the second region and the third region, the device being formed at least partially in the planar device layer.
 14. The structure of claim 7, wherein the first lateral edge is directly over the top surface of the dielectric layer.
 15. The structure of claim 7, wherein the dielectric layer further defines a second opening from the top surface to the substrate, a fourth region of the second crystalline material being in the second opening, defects arising from the lattice mismatch within the fourth region terminating at a sidewall of the second opening, a fifth region of the third crystalline material being over the fourth region, the fifth region having a second lateral edge extending higher than the top surface of the dielectric layer, the third region of the fourth material being disposed adjacent the second lateral edge.
 16. A structure comprising: a first dielectric sidewall, a dielectric surface, and a second dielectric sidewall over a substrate comprising a first crystalline material, the dielectric surface extending from an upper edge of the first dielectric sidewall to an upper edge of the second dielectric sidewall; a first region of a second crystalline material over the substrate and extending above the upper edge of the first dielectric sidewall, the second crystalline material being lattice mismatched to the first crystalline material, defects arising from the lattice mismatch within the first region terminating at the first dielectric sidewall, the first region having a first lateral edge above the dielectric surface; a second region of the second crystalline material over the substrate and extending above the upper edge of the second dielectric sidewall, defects arising from the lattice mismatch within the second region terminating at the second dielectric sidewall, the second region having a second lateral edge above the dielectric surface; a third material over the dielectric surface and disposed between the first lateral edge and the second lateral edge, the second crystalline material in respective portions of the first region and the second region above the respective upper edges being less defective than the third material; and a device formed in and/or above at least one of the first region and the second region.
 17. The structure of claim 16, wherein the third material is a different material from the second crystalline material.
 18. The structure of claim 16, wherein the third material is amorphous.
 19. The structure of claim 16, wherein the third material is polycrystalline.
 20. The structure of claim 16 further comprising a planar device layer over the second crystalline material and the third material, the device being formed at least partially in the planar device layer. 